New tio2-ag nanoparticles used for organic compounds degradation
1 Complutense University of Madrid, Faculty of Chemical, Department of Materials and Chemical Engineering, Av. S neca, 2, 28040 Madrid, Spain
2 Gheorghe Asachi Technical University of Iasi, Faculty of Chemical Engineering and Environmental Protection, Chemical Engineering Department, 73 Prof.dr.doc. Dimitrie Mangeron Street, 700050 Iasi, Romania
3 Alexandru Ioan Cuza University of Iasi, Blvd. Carol I No 11, 700506 Iasi, Romania
4 University of Pannonia, 10 Egyetem St. Veszpr m, 8200 Hungary
5 Gheorghe Asachi Technical University of Iasi, Faculty of Chemical Engineering and Environmental Protection, Department of Environmental Engineering and Management, 73 Prof.dr.doc. Dimitrie Mangeron Street, 700050 Iasi, Romania
2 Gheorghe Asachi Technical University of Iasi, Faculty of Chemical Engineering and Environmental Protection, Chemical Engineering Department, 73 Prof.dr.doc. Dimitrie Mangeron Street, 700050 Iasi, Romania
3 Alexandru Ioan Cuza University of Iasi, Blvd. Carol I No 11, 700506 Iasi, Romania
4 University of Pannonia, 10 Egyetem St. Veszpr m, 8200 Hungary
5 Gheorghe Asachi Technical University of Iasi, Faculty of Chemical Engineering and Environmental Protection, Department of Environmental Engineering and Management, 73 Prof.dr.doc. Dimitrie Mangeron Street, 700050 Iasi, Romania
Abstract
TiO2-assisted photocatalysis is used in numerous environmental applications and for the manufacturing of different products. Ag-doped TiO2 nanoparticles were synthesized by impregnation using silver nitrate solution on TiO2 obtained by sol-gel method and on commercial Degusa P25 (Evonik). Silver is widely studied as a dopant for semiconductor materials, due to its antibacterial properties. In addition to this, it acts as electron sink and donor for photogenerated electrons, enhancing the photocatalytic activity. The physical properties of the samples calcined at different temperatures were investigated by XRD, XRF, SEM, TEM, SAED and EDAX techniques. The calcination temperature of 650oC led to the total transformation of titanium dioxide (anatase) to rutile phase when commercial P25 was doped with Ag. In the case of samples produced by sol-gel method, the anatase is still the major phase even at this temperature. The photocatalytic activity of the synthesized catalysts was evaluated in the UV-assisted photodegradation of Rhodamine 6G and Congo Red dyes. The conversion yield of Rhodamine 6G reached 66.5% and that of Congo Red was 53% after 120 minutes of irradiation.
Keywords
photocatalysis; photodegradation; silver; titanium oxide